Water Retention in Kenaf/Polypropylene Composites Due to Repeated Immersion and Drying Conditions

摘要

Lignocelluloses based natural fibers composites are very prone to water absorption due to OH functional group within cellulose and hemicelluloses of natural fibers. In this work, the water retention in the kenaf/polypropylene (kenaf /PP) composite due to repeated immersion and drying are studied. The composites (40%, 50%, 60% and 70% fiber loading) are immersed in the water and then dried in room condition (24°C and 48 % humidity) for 4 cycles (1 cycle is 10 days of immersion and drying). The parameters are 82 (imply 8 days immersion 2 days drying), 64, 46 and 28 per cycle. Continuous immersion (100% immersion) is used as a reference of water absorption behavior of the composite. The results for 70% fiber loading under minimum drying days of 82, shows that the water retention reduced to 36% from the water absorbed and further drying only reduced to 31%. When the experiment are repeated for several cycles, 70% fiber loading composites shows a decreasing pattern in water retention at the second cycle whereas 40% fiber loading composite showing an increasing pattern. Duration of immersiondrying does play an important role in the amount of water retention in the composite. The water retention of the composites either show an increasing or decreasing pattern depending on kenaf fiber loading and repetition of the immersiondrying for several cycles.