One-axis-oriented crystal growth of lead zirconate titanate thin films on metal substrates using perovskite-type oxide nanosheet layer

机译:使用Perovskite型氧化物纳米晶片层对金属基材上的铅锆钛酸铅薄膜的单轴导向晶体生长

获取原文

摘要

One-axis-oriented Pb(Zr,Ti)O_3 (PZT) films were fabricated using a chemical solution deposition technique on (111 )Pt/TiO_2/( 100)Si and Inconel625 substrates buffered by nanosheet Ca_2Nb_3O_(10) (ns-CN). The (001)-oriented PZT crystals (Zr/Ti=0.40:0.60, tetragonal) were preferentially grown on (001)ns-CN/Inconel625, whereas the PZT crystals deposited on (001)ns-CN/(111)Pt/ TiO_2/(100)Si exhibited preferential PZT(100) orientation. The resulting PZT film on (001 )?5-CN/InconeI625 indicated remanent polarization of approximately 59 μC/cm~2, which was significantly larger than that on (001)ns-CN/(111l)Pt/TiO_2/(100)Si.
机译:使用纳米液Ca_2NB_3O_(10)缓冲的(111)Pt / TiO_2 /(100)Si和Inconel625基材的化学溶液沉积技术制造了一种轴上的Pb(Zr,Ti)O_3(PZT)膜。(NS-CN )。 (001)的PZT晶体(Zr / Ti = 0.40:0.60,四边形)优先生长在(001)NS-CN / Inconel625上,而PZT晶体沉积在(001)NS-CN /(111)Pt / TiO_2 /(100)SI表现出优先PZT(100)方向。 得到的PZT膜(001)?5-CN / INCONEI625指示约59μC/ cm〜2的重新偏振,其显着大于(001)NS-CN /(111L)PT / TiO_2 /(100) Si。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号