METALLOGRAPHIC EVALUATION OF A BREACHED CONTAINER

摘要

During an annual inventory of nuclear material, a plated steel container which contained plutonium oxide failed. The container had been packaged for temporary storage but had been overlooked and remained in storage for more than 23 years. Although it was determined that the failure occurred through the slip-top rim, a metallurgical evaluation was requested to help to determine the integrity of the container.Optical metallography and scanning electron microscopy were used to analyze the character and degree of corrosion in the container. The depth of corrosion, measured at approximately 10 jam, did not pose a threat to the integrity of the container. However, the corrosion morphology and chemistry did suggest that a galvanic cell had developed between the tin and steel from the condensation of water. The morphology also suggests that the attack of the steel took place over a series of cycles due to changes of the environment.