Microstructure Evolution during Combustion Synthesis of Ni/Ni-Aluminide Laminated Composites

摘要

Combustion reaction in laminated Ni and Al foils was ignited by plasma activated sintering (PAS) to synthesize metal-intermetallic laminated composites (MILCs). The microstructure evolution in the reaction and the post-heat treatment was investigated. The results showed that thermal explosion (TE) reaction were happened between Ni and Al foils at the melting point of Al. The reaction was incomplete due to the heat loss through the thick foils. The produced phases, Ni_2Al_3 and NiAl_3, were converted to a compositionally gradient series of intermetallic phases in the final microstructures of the intermetallic layers after the post heat treatment.