Microstructure and Properties of Calcium Borosilicate and Borosilicate Glass-Ceramic Composites

摘要

Calcium borosilicate (CaO-B_2O_3-SiO_2, CBS) glass based glass-ceramic composites were prepared by introducing borosilicate glass. The effects of borosilicate glass and firing temperature on the microstructure and properties of the glass-ceramic composites were investigated. The results showed that the composites containing 0～40% (in mass fraction, the same below) borosilicate glass can be sintered at 850℃. The dielectric constant (ε_r) decreases with the increase of borosilicate glass content and can be adjusted in the range of 5.6～6.6. The coefficient of thermal expansion (CTE) increases with the increase of borosilicate glass content. Increasing sintering temperature favors the precipitations of crystal phases, which have lower ε_r than CBS glass, resulting in the decrease of ε_r for the composites.