Grain-oriented electrical steel sheet excellent in magnetic properties and excellent in adhesion of the primary coating to the steel sheet is provided. The grain-oriented electrical steel sheet according to the present invention is provided with a base metal steel sheet containing a chemical composition containing, by mass %, C: 0.005% or less, Si: 0.5 to 7.0%, Mn: 0.05 to 1.00%, a total of S and Se: 0.005% or less, sol. Al: 0.005% or less, and N: 0.005% or less and having a balance comprised of Fe and impurities and with a primary coating formed on a surface of the base metal steel sheet and containing Mg2SiO4as a main constituent, wherein a peak position of Al emission intensity obtained when performing elemental analysis by glow discharge optical emission spectrometry from a surface of the primary coating in a thickness direction of the grain-oriented electrical steel sheet is arranged within a range of 2.0 to 12.0 μm from the surface of the primary coating in the thickness direction, and a number density of Al oxides of a size of 0.1 μm or more in terms of a circle equivalent diameter based on the area at the peak position of Al emission intensity is 0.03 to 0.2/μm2.
展开▼