Aluminum alloy fin material for heat exchanger excellent in strength, electrical conductivity, and brazeability, method for manufacturing aluminum alloy fin material for heat exchanger, and heat exchanger comprising aluminum alloy fin material for heat exchanger

摘要

An aluminum alloy fin material for a heat exchanger in the present invention comprises an aluminum alloy having a composition containing Mn: 1.2 to 2.0%, Cu: 0.05 to 0.20%, Si: 0.5 to 1.30%, Fe: 0.05 to 0.5%, and Zn: 1.0 to 3.0% by mass and a remainder comprising Al and an unavoidable impurity, further containing one or two or more of Ti: 0.01 to 0.20%, Cr: 0.01 to 0.20% and Mg: 0.01 to 0.20% by mass as desired, and, after heating in brazing, has a tensile strength of 140 MPa or more, a proof stress of 50 MPa or more, an electrical conductivity of 42% IACS or more, an average grain diameter of 150 μm or more and less than 700 μm, and a potential of −800 mV or more and −720 mV or less.