High-strength steel with yield strength of 800 MPa and production method therefor

摘要

A high-strength steel having a yield strength at a level of 800 MPa and a method of manufacturing the same, with the components and amounts thereof by weight percentage being: C: 0.06-0.14%, Si: 0.1-0.30%, Mn: 0.8-1.60%, Cr: 0.2-0.70%, Mo: 0.1-0.40%, Ni: 0-0.30%, Nb: 0.01-0.030%, Ti: 0.01-0.030%, V: 0.01-0.05%, B: 0.0005-0.0030%, Al: 0.02-0.06%, Ca: 0.001-0.004%, N: 0.002-0.005%, P≤0.02%, S≤0.01%, O≤0.008%, the balance of Fe and unavoidable impurities; wherein the above elements meet the following relationships: 0.40%