Release film for vehicle decoration adhesive sheet, laminated film for vehicle decoration adhesive sheet and vehicle decoration adhesive sheet
Release film for vehicle decoration adhesive sheet, laminated film for vehicle decoration adhesive sheet and vehicle decoration adhesive sheet
PROBLEM TO BE SOLVED: To provide a release film having no wrinkles or irregularities and having excellent releasability even when used for vehicle decoration, and to have high gloss using the releasable film, scratch resistance, curved surface followability, and sticking. Provision of laminated films suitable for various uses, including marking films with good workability, and vehicle decoration adhesive sheets using the same. SOLUTION: For a vehicle decorative adhesive sheet containing a base film showing elongation (i) in the following range when subjected to thermomechanical analysis under the following conditions and having a release layer on at least one side of the base film. Release film. Test piece size: width 4 mm x length 40 mm, distance between chucks: 8 mm, measurement atmosphere: under nitrogen atmosphere (nitrogen flow rate 100 ml / min), temperature rise rate: 10 ° C / min (start temperature: 23 ° C, end) Temperature: 240 ° C.), Load: 400 mN, Absolute value of elongation of the base film at 125 ° C. is 40 μm or less [Selection drawing] None
展开▼
机译:要解决的问题:提供一种没有皱纹或不规则性的剥离膜,即使用于车辆装饰,也具有优异的可剥离性,并且使用可释放薄膜,耐刮擦,曲面跟随和粘附性高光泽度。提供适用于各种用途的层压膜,包括具有良好的可加工性的标记膜,以及使用该薄膜的标记膜。溶液:当在下列条件下进行热机械分析并在基膜的至少一侧具有剥离层时,用于含有基部膜的车辆装饰粘合片,其显示在下列范围内的基础膜。释放膜。 <条件>试验片尺寸:宽度4 mm x长度40 mm,卡盘之间的距离:8 mm,测量气氛:在氮气氛下(氮流速100 ml / min),升温速率:10°C / min(开始温度:23°C,末端)温度:240℃,载荷:400mn,<伸长(i)>在125℃下的基膜伸长的绝对值为40μm或更小[选择图]无
展开▼