A supporting member for positioning in engagement with the screen or felt of a paper or cardboard machine for drainage and for sheet forming consists of one or more ceramic components of hard, dense sintered aluminium oxide having the following features: (1) a content of Al2O3 of from 97% to 98.5% by weight, a content of MgO of 0.5 +/- 0.3% by weight, and a content of SiO2 of from 1% to 2.5% by weight; (2) a Synder-Graff grain size of 5 mu m +/- 2 mu m; (3) a Vickers hardness of more than 1600 daN/mm2 at a testing load of 0.2 daN/mm2; (4) a bending strength of at least 300N/mm2; (5) a transcrystalline fracture proportion of more than 70% and (6) a surface characteristic specified by (a) a roughness of Ra 0.2 mu m, measured with a feeler needle having a radius of 3 mu m on a polished surface (b) a proportion of pores in the surface of less than 10%, and (c) a mean (median) pore size 5 mu m.
展开▼
机译:用于与造纸机或纸板机的筛子或毛毡啮合以进行排水并用于片材成型的支撑构件,由一种或多种硬质致密氧化铝的陶瓷成分组成,具有以下特征:(1)Al2O3的含量含量为97-98.5%(重量),MgO含量为0.5 +/- 0.3%(重量),SiO2含量为1%至2.5%(重量); (2)Synder-Graff晶粒度为5微米+/- 2微米; (3)在0.2daN / mm 2的测试载荷下的维氏硬度大于1600daN / mm 2; (4)抗弯强度至少为300N / mm 2; (5)大于70%的跨晶断裂率和(6)由(a)粗糙度Ra <0.2μm规定的表面特性,该粗糙度是用半径为3μm的触针在抛光表面上测得的b)表面孔隙的比例小于10%,并且(c)平均(中值)孔径小于5微米。
展开▼