MANUFACTURE OF HIGH TOUGHNESS NONTEMPERED HIGH TENSILE STEEL SHEET SUPERIOR IN WELDABILITY AND CAUSING LESS SEPARATION
MANUFACTURE OF HIGH TOUGHNESS NONTEMPERED HIGH TENSILE STEEL SHEET SUPERIOR IN WELDABILITY AND CAUSING LESS SEPARATION
展开▼
机译:高韧性非回火高强度钢板在可焊性和成因的降低方面的优势
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE:To obtain the titled high tensile steel sheet by heating the steel containing specified amount of C, Si, Mn, Al to the specified temp. range, performing two stage rolling with the specified cumulative draft and cooling at the specified cooling rate. CONSTITUTION:The steel consists of, by weight %, 0.03-2 C, 0.03-0.6 Si, 0.5- 2 Mn, 0.005-0.06 Al if necessary, one or =2 kinds among and the balance Fe with inevitable impurities (where 0.008 S in the inevitable impurities). This steel is heated to 900-1,150 deg.C, then rolled with the cumulative draft R satisfying the equation calculated for the heating temp. T when the heated temp. is above 900 deg.C until it is decreased to 900 deg.C; then rolling is continued with the cumulative draft above 50% during the temp. is reduced from 900 deg.C to Ar3 point and the rolling is finished at below Ar3 temp. This steel is then cooled at the rate of 2-25 deg.C/sec.
展开▼