摘要
PURPOSE:To obtain an Al alloy having strong cast-welding power, by letting Al contain specified amounts of one or more of Si, Mg, Cr, Ti and Zr. CONSTITUTION:The composition of a cast-welding Al alloy is determined as, by wt%, one or more of 2-6 Si, 1.2-9 Mg, 0.4-1 Cr and 0.15-0.8 Zr, and the balance Al and inevitable impurities. A steel pipe, degreased by sand-blasting and preheated at 800 deg.C or so, is located in a main mold 2a. The melt 5a of said cast-welding Al alloy is poured into the main mold 2a. After the laps of 15sec, the melt 5a is charged with hydrostatic pressure of 200kg/cm2 or more by pressing it with a press punch 6a. When the steel pipe is welded to an Al alloy by use of the welded joint formed in this way, the welded article satisfying pressure-resistance and joint strength is obtained.
展开▼
机译:目的:为了获得具有强大的铸造焊接能力的铝合金,方法是让Al包含指定量的Si,Mg,Cr,Ti和Zr中的一种或多种。组成:铸造焊接铝合金的成分以重量百分比确定为2-6 Si,1.2-9 Mg,0.4-1 Cr和0.15-0.8 Zr中的一种或多种,其余为Al和不可避免的杂质。在主模具2a中设置有通过喷砂处理而脱脂并在800℃左右预热的钢管。将所述铸造焊接铝合金的熔体5a倒入主模具2a中。 15秒后,通过用冲压机6a对其加压而使熔体5a充入200kg / cm 2或更高的静水压力。当通过以这种方式形成的焊接接头将钢管焊接到铝合金上时,获得了满足耐压性和接头强度的焊接物品。
展开▼