A PROCESS FOR PRODUCING COLD REDUCED SILICON STEEL STRIP AND SHEET OF LESS THAN 0.30MM THICKNESS HAVING THE CUBE-ON-EDGE ORIENTATION
A PROCESS FOR PRODUCING COLD REDUCED SILICON STEEL STRIP AND SHEET OF LESS THAN 0.30MM THICKNESS HAVING THE CUBE-ON-EDGE ORIENTATION
展开▼
机译:厚度小于0.30mm的冷轧硅钢带和薄板的生产工艺
展开▼
页面导航
摘要
著录项
相似文献
摘要
pA process for producing silicon steel strip of less than 0.30 mm thickness having cube-on-edge orientation, which comprises heating a silicon steel slab to 1300 DEG -1400 DEG C., hot rolling to hot band thickness, removing hot mill scale, cold rolling to intermediate thickness without annealing the hot rolled band, subjecting the intermediate thickness cold rolled material to an intermediate anneal at a temperature of 1010 DEG to about 1100 DEG C. with a total time of heating and soaking of less than about 180 seconds, cold rolling to a final thickness of less than 0.30 mm, decarburizing, applying an annealing separator, and finally annealing in conventional manner./p[US4478653A]