Nickel-base superalloy for castings, free from Laves phase, and treated by means of hot isostatic pressing
Nickel-base superalloy for castings, free from Laves phase, and treated by means of hot isostatic pressing
展开▼
机译:用于铸造的镍基高温合金,无拉夫斯相,并通过热等静压处理
展开▼
页面导航
摘要
著录项
相似文献
摘要
A nickel base superalloy composition for castings, subjected to hot isostatic pressing and subsequent heat treatment is described. The invention alloy has an as-cast microstructure which is substantially free from Laves phase, even at slow solidification rates. As a result, the alloys is significantly more weldable than IN7l8. The alloy consists of:Ni + Co 50 to 66 wt %Cr 10 to 15 wt %Mo 0 to 3,3 wt %Nb + Ta 4,75 to 5,5 wt %Ti 0,65 to 1,15 wt %Al 0,4 to 0,8 wt %Fe 15 to 24 wt %
展开▼
机译:描述了一种用于铸件的镍基高温合金组合物,该组合物经过热等静压和随后的热处理。本发明的合金具有即使在较慢的凝固速率下也基本上没有拉夫斯相的铸态组织。结果,该合金比IN718的焊接性要好得多。该合金包括:Ni + Co 50至66 wt%Cr 10至15 wt%Mo 0至3.3 wt%Nb + Ta 4.75-5.5 wt%Ti 0.65至1.15 wt%Al 0.4至0.8重量%Fe 15至24 wt%