Superplastic forging of zirconia ceramics
Superplastic forging of zirconia ceramics
展开▼
机译:氧化锆陶瓷的超塑性锻造
展开▼
页面导航
摘要
著录项
相似文献
摘要
The invention relates to producing relatively flaw free zirconia ceramic shapes requiring little or no matching by superplastic forging of a fully sintered or partially sintered preform. The preform is prepared by providing a starting powder comprising by weight from about 70% to about 100% zirconia and from about 0 to about 30% of stabilizing additives, e.g. commerically available TZ-3Y powder, cold pressing to obtain a preform of green density ranging from about 30% of theoretical density to about 75% of theoretical density and partially or fully sintering at atmospheric pressure, e.g. in argon or air at a temperature ranging from about 900° C. to about 1900° C. The superplastic forging is carried out by isothermally pressing the partially or fully sintered preform into substantially final shape utilizing a temperature and strain rate such that surface cracks do not occur, e.g. utilizing a temperature of 1310° C., a substantially constant displacement rate based on an initial strain rate of 7×10. sup.-3 seconds .sup.-1 and open die or closed die processing in a graphite or metal die.
展开▼