ALUMINA IN FORM SPHERICAL NON-AGGREGATED PARTICLES HAVING NARNOW SIZE DISTRIBUTION AND SIZE BELOW 2 MICRONS AND PROCESS FOR PREPARING SAME
ALUMINA IN FORM SPHERICAL NON-AGGREGATED PARTICLES HAVING NARNOW SIZE DISTRIBUTION AND SIZE BELOW 2 MICRONS AND PROCESS FOR PREPARING SAME
展开▼
机译:具有纳氏尺寸分布且尺寸小于2微米的球形非聚集颗粒形式的氧化铝及其制备方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Alpha alumina consisting essentially of solid, spherical, non- aggregated particles, is characterized by having a number average diameter from 0.06 to 2 micro meter, a polydispersion index dw/dn less than or equal to 2.0 wherein dw is the weight average diameter and dn is the number average diameter, a total porosity of micro/meso type of less than 0.3 cc/g, a specific surface area from 0.7 to 80 meter power 2/g, and an apparent density of the particles of from 3.2 to 3.94 g/Cm power 3.
展开▼
机译:主要由固体,球形,非聚集颗粒组成的α-氧化铝的特征在于其数均直径为0.06至2微米,多分散指数dw / dn小于或等于2.0,其中dw为重均直径,dn是数均直径,小于0.3 cc / g的微米/介孔型总孔隙率,比表面积为0.7至80米2 / g,表观密度为3.2至3.94 g / g厘米功率3。