Manufacturing process for superconductor of Bi-Pb-Sr-Ca-Cu-O series
Manufacturing process for superconductor of Bi-Pb-Sr-Ca-Cu-O series
展开▼
机译:Bi-Pb-Sr-Ca-Cu-O系列超导体的制造工艺
展开▼
页面导航
摘要
著录项
相似文献
摘要
A manufacturing process of a high temperature superconductor is disclosed. First, powders of Bi₂O₃ , SrCo₃ , CaCo₃ , CuO and PbO are measured in the ratios of 1.4 : 0.6 : 2 : 2 : 3.8, and then, they are crushed and mixed together by means of a ball mill. Then the mixture is calcinated two or three times at a temperature of 600 - 800° C for 24 - 48 hours, and then, sintering is carried out at a temperature of 800 - 900° C for 48 hours. Then a cold pressing and a hot pressing are carried out, and finally a sintering is carried out for two days. According to the present invention, the manufacturing period is shortened.
展开▼
机译:公开了高温超导体的制造方法。首先,以1.4∶0.6∶2∶2∶2∶3.8的比例测量Bi 2 O 3,SrCo 3,CaCo 3,CuO和PbO的粉末,然后将它们粉碎并用球磨机混合在一起。然后将混合物在600-800℃的温度下煅烧两次或三次24-48小时,然后在800-900℃的温度下烧结48小时。然后进行冷压和热压,最后进行两天的烧结。根据本发明,缩短了制造周期。