HIGH STRENGTH ALLOY STEEL FOR INJECTION MOLDING AND POWDER METALLURGY
HIGH STRENGTH ALLOY STEEL FOR INJECTION MOLDING AND POWDER METALLURGY
展开▼
机译:注射成型和粉末冶金用高强度合金钢
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: To provide alloy steel for injection molding and powder metallurgy having much higher strength and slightly lower elongation than a conventional Fe-Ni-C alloy. ;CONSTITUTION: A blend having a compsn. consisting of 1-10wt.% Cu, 1-10wt.% Ni, 0.3-1wt.% C and the balance Fe is kneaded with an org. binder and injection molded. The resulting compact is freed of the binder and sintered to obtain a sintered compact having 93.2kg/mm2 tensile fracture strength and 10.6% elongation. The elongation is slightly lower than that (15.7%) of an Fe-Ni-C alloy but the tensile fracture strength is much higher than that (51.3kg/mm2) of the Fe-Ni-C alloy.;COPYRIGHT: (C)1993,JPO&Japio
展开▼
机译:用途:提供用于注射成型和粉末冶金的合金钢,其强度比传统的Fe-Ni-C合金高得多,而伸长率则稍低。 ;组成:具有compsn的混合。由1-10wt。%的Cu,1-10wt。%的Ni,0.3-1wt。%的C和其余的Fe组成的有机物与有机物捏合。粘合剂和注塑成型。所得的压坯不含粘合剂并进行烧结,从而获得具有93.2kg / mm 2 Sup>拉伸断裂强度和10.6%的伸长率的烧结压坯。伸长率比Fe-Ni-C合金的伸长率稍低(15.7%),但拉伸断裂强度比Fe-Ni-C合金的伸长率(51.3kg / mm 2 Sup>)高得多。合金;版权:(C)1993,JPO&Japio
展开▼