The present invention relates to a polyamide dope cord yarn having a strength utilization rate of 95% or more and a strength of 8.0 g / d or more, a cut elongation of 20% or more and a crystallinity of 40% or more, Polyamides were melt-spun, stretched in four or more stages, and heat-treated to produce a polyamide stretched yarn having a cut elongation of 30% or more, a strength of 7.5 g / d or more, and a crystallinity of 15 to 30% And more than 5% of tension is applied in the section.;The polyamide dope cord of the present invention has high strength utilization (95% or more), high strength and high toughness.
展开▼
机译:本发明涉及强度利用率为95%以上且强度为8.0g / d以上,断面伸长率为20%以上且结晶度为40%以上的聚酰胺掺杂帘线。熔融纺丝,经过四个或更多阶段的拉伸,并进行热处理,以生产出具有30%或更高的断面伸长率,7.5 g / d或更高的强度以及15%至30%的结晶度的聚酰胺拉伸纱线;在该部分中施加大于5%的张力。本发明的聚酰胺涂料帘线具有高强度利用率(95%以上),高强度和高韧性。
展开▼