Production manner null of the cement non content monolithic refractory which uses the cement non content monolithic refractory raw materials and these
Production manner null of the cement non content monolithic refractory which uses the cement non content monolithic refractory raw materials and these
展开▼
机译:使用水泥无含量整体耐火原料的水泥无含量整体耐火材料的生产方式及这些
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE:To obtain the subject refractory with enhanced corrosion resistance to chemical attack by molten slag, etc., and to fine resistance by adding a small amount of a dispersing agent to a refractory composition composed of an aggregate, intermediate powder and fine powder as the refractory composition and one or more ultrafine powders such as silica and hydraulic alumina having a prescribed grain diameter. CONSTITUTION:The objective cementless monolithic refractory (I) obtained by preparing a refractory material, composed of an aggregate, intermediate powder and fine powder, e.g. bauxite or a high purity alumina, alone or as mixture, further preparing a refractory composition (I') composed of =60wt.% aforementioned refractory material (I), 2-20wt.% ultrafine powder composed of one or more of silica, alumina, etc., or chromite and 2-10wt.% hydraulic alumina, contained in the above-mentioned ultrafine powder and having 3-15mum average grain diameter and then adding 0.2wt.% dispersing agent to the aforementioned refractory composition (I'). Low-melting compounds are prevented from the forming by the absence of the cement and hot characteristics such as corrosion, fire resistance, high-temperature strength, etc., are improved by combination of the hydraulic alumina and dispersing agent.
展开▼