Use of a Zn-Ni alloy for preparation of Zn-Ni alloy electroplating bath, use of a Zn-Ni alloy for preparation of Zn-Ni alloy hot-dip galvanizing plating bath, and method for producing a Zn-Ni alloy
Use of a Zn-Ni alloy for preparation of Zn-Ni alloy electroplating bath, use of a Zn-Ni alloy for preparation of Zn-Ni alloy hot-dip galvanizing plating bath, and method for producing a Zn-Ni alloy
A Zn-Ni alloy having a high Ni content is used for supplying Ni²⁺ and Zn²⁺ ions into an acidic plating bath and for supplying Ni and Zn into a hot dip galvanizing bath. This alloy is characterized by being produced by using a flux consisting of a fused-salt former, which forms a salt having a melting temperature of 700°C or less, and Na₂B₄O₇ and occasionaly additionally Na₂CO₃. By using the inventive alloy, the bath can be quickly prepared, and Zn and Ni can be supplied to the bath without leaving the undissolved residue.
展开▼
机译:具有高Ni含量的Zn-Ni合金用于将Ni 2+和Zn 2+离子供应到酸性镀浴中以及用于将Ni和Zn供应到热浸镀锌浴中。该合金的特征在于使用由熔盐形成剂和Na 2 B 3 O 3,有时还包括Na 2 CO 3组成的熔剂生产,该熔剂形成熔融温度为700℃或更低的盐。通过使用本发明的合金,可以快速制备浴液,并且可以将锌和镍供应至浴液而不会留下未溶解的残留物。
展开▼