Manufacturing method of high carbon steel wire rod excellent in mechanical peeling property of scale
Manufacturing method of high carbon steel wire rod excellent in mechanical peeling property of scale
展开▼
机译:鳞片机械剥离性能优异的高碳钢线材的制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a method for producing a high carbon steel wire rod, which, after hot rolling at the time of producing a high carbon steel wire rod, controls a proper laying head temperature and a strict cooling rate to maintain excellent mechanical properties and microstructure, It is an object of the present invention to provide a high carbon steel wire rod excellent in mechanical peelability.;The present invention relates to a method for producing a high carbon steel wire rod containing 0.4 to 1.2% by weight of carbon (C), characterized in that the cooling starting temperature after hot rolling is 850-900C and the average cooling rate The cooling rate from 680C to 200C was cooled to 15-25C / sec based on the cooling rate at the moment of passing through 680C, so that the temperature of the FeO layer And a method for producing a high-carbon steel wire rod excellent in mechanical peelability of scale by keeping the thickness uniformly at 10-15 .
展开▼