Synthesis of bi18?pb04?sr2ca2cu3ox superconductors
Synthesis of bi18?pb04?sr2ca2cu3ox superconductors
展开▼
机译:bi18?pb04?sr2ca2cu3ox超导体的合成
展开▼
页面导航
摘要
著录项
相似文献
摘要
Two-powder processes for the synthesis of superconducting (Bi, Pb)-2223/Ag-clad wires by the oxide-powder-in-the-robe are provided. The first precursor powder, of nominal stoichiometry CaCuOx, is a solution-synthesized mixture of Ca0.45Cu0.55O2 and CaO. Using these oxide precursor mixtures, superconducting tapes with well-aligned grains and reproducible critical current densities Jc in the range of 20,000 to 26,000 A/cm2 at 75 K in self-field after annealing less than 200 hours were obtained.
展开▼
机译:提供了通过长袍氧化物粉末合成超导电(Bi,Pb)-2223 / Ag包覆线的两粉末工艺。标称化学计量为CaCuOx的第一种前体粉末是Ca0.45Cu0.55O2和CaO的溶液合成混合物。使用这些氧化物前体混合物,在不到200小时的退火后的自励磁场中,在75 K的条件下,获得了晶粒排列整齐且临界电流密度Jc在20,000至26,000 A / cm2范围内的超导带。