Iron-based amorphous alloy with excellent magnetic properties and excellent fracture resistance and manufacturing method
Iron-based amorphous alloy with excellent magnetic properties and excellent fracture resistance and manufacturing method
展开▼
机译:具有优异的磁性能和优异的抗断裂性的铁基非晶合金及其制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
1. TECHNICAL FIELD OF THE INVENTION;An iron-based amorphous alloy having excellent magnetic properties and excellent fracture resistance, and a manufacturing method thereof.;2. The technical problem to be solved by the invention;When the amount of Mn added is 0.2at% or more and less than 0.5at%, iron loss can be improved without lowering the magnetic flux density, and the rapid solidification treatment of the molten metal is carried out in an atmosphere of CO 2 containing a small amount of H 2 . It also improves the surface smoothness of the thin ribbon and also reforms the oxidation state.;3. Summary of Solution to Invention;Fe x B y Si z Mn a where 75 ≤ X ≤ 82 at%, 7 ≤ Y ≤ 15 at%, 7 ≤ Z ≤ 0.5 at%, wherein the surface smoothness is less than 0.8 μm as the centerline average smoothness R a Amorphous alloys and methods of manufacturing the same.;4. Important uses of the invention;Iron core material for transformers and other amorphous alloys.
展开▼
机译:1.具有优异的磁性能和优异的抗断裂性的铁基非晶合金及其制造方法。本发明要解决的技术问题;当Mn的添加量为0.2at%以上且小于0.5at%时,可以在不降低磁通密度的情况下改善铁损,并且可以对熔融金属进行快速凝固处理。在含有少量H 2 Sub>的CO 2 Sub>气氛中进行。它还提高了薄带的表面光滑度,并改变了氧化态。3。 Fe x Sub> B y Sub> Si z Sub> Mn a Sub>其中75≤ X < / Sub>≤82 at%,7≤ Y Sub>≤15 at%,7≤ Z Sub>≤0.5 at%,其中表面光滑度小于0.8μm作为中心线平均光滑度R a Sub>非晶态合金及其制造方法; 4。本发明的重要用途;铁心材料,用于变压器和其他非晶态合金。
展开▼