Method of manufacturing the excellent alloyed molten Zn-plated steel sheet to low temperature chipping resistance
Method of manufacturing the excellent alloyed molten Zn-plated steel sheet to low temperature chipping resistance
展开▼
机译:具有优异的耐低温崩裂性的优质合金熔融镀锌钢板的制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: To improve low temp. chipping resisting property by galvanizing a base steel sheet ground by a prescribed thickness by hot dip zinc-coating, then, limiting the Fe content in a plated film by heating for alloying at a prescribed temp. rising rate. ;CONSTITUTION: A fresh surface is disclosed by previously grinding the surface of the base steel sheet by 0.1 to 5g/m2 thickness. The ground steel sheet is galvanized by hot dix zinc-coating and then heated for alloying in the region of 420 to 650°C plate temp. at 20°C/sec or higher temp. rising rate. Fe content in the plated film is limited to 7 to 13wt.% and only the boundary of the steel sheet-plating is made to be a high Fe content. In such a manner, both prevention of stripping caused by chipping generating at the boundary of the plating-steel sheet and maintenance of the powdering resistance and sacrifice corrosion inhibition capability are made compatible with each other.;COPYRIGHT: (C)1994,JPO&Japio
展开▼
机译:目的:改善低温。通过热浸镀锌对被研磨成规定厚度的基体钢板进行镀锌处理,然后通过在规定温度下进行合金化加热来限制镀膜中的Fe含量,从而具有耐剥落性。上升率。 ;组成:通过预先将基础钢板的表面打磨至0.1至5g / m 2 Sup>的厚度来公开新表面。磨碎的钢板通过热dix锌镀锌,然后在板温420至650°C的范围内加热以进行合金化。在20°C /秒或更高的温度下上升率。镀覆膜中的Fe含量被限制为7至13wt。%,并且仅使钢板镀层的边界为高Fe含量。这样,既可以防止在电镀钢板的边界处产生碎屑引起的剥落,又可以保持耐粉化性和牺牲腐蚀抑制能力,两者兼具。COPYRIGHT:(C)1994,JPO&Japio
展开▼