PROBLEM TO BE SOLVED: To execute float-up and separation of fine inclusions by controlling the flowing state of molten steel in a tundish for continuous casting. ;SOLUTION: The inclusion removing method is the method for floating up and separating the inclusion in the molten steel in the tundish at the time of continuously casting, and at the time of using V (m3/min) for the molten steel pouring quantity into the tundish at the stationary time, S (m2) for the cross sectional area at the right angle to the shifting direction of the narrowest part of the molten steel stream in the tundish, H (m) for the molten steel depth of the molten steel stream and L (m) for the horizontal distance between both nozzle centers of the pouring and the flowing-out, the molten steel stream in the tundish is controlled so as to satisfy the following conditions. V/D=0.28-0.50 m/min, L/H=5-10.;COPYRIGHT: (C)1998,JPO
展开▼
机译:解决的问题:通过控制连续浇铸中间包中钢水的流动状态,实现细小夹杂物的浮起和分离。 ;解决方案:夹杂物去除方法是在连铸时和使用V(m 3 Sup> / min时,将中间包中的钢水中夹杂物漂浮并分离的方法。 )对于固定时间进入中间包的钢水量,S(m 2 Sup>)为与钢水最窄部分的移动方向成直角的横截面积将中间包中的钢水流的钢水深度H(m)和浇注和流出的两个喷嘴中心之间的水平距离的L(m)进行控制,从而将中间包中的钢水流控制为满足以下条件。 V / D = 0.28-0.50 m / min,L / H = 5-10 .;版权:(C)1998,日本特许厅
展开▼