Continuous casting method of special welded broom casting with excellent internal quality
Continuous casting method of special welded broom casting with excellent internal quality
展开▼
机译:内部质量优良的特殊焊接扫帚铸件的连铸方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a continuous casting method of a bloom used for special welding wires such as CO 2 welding, MIG welding, and MAG welding. In providing.;The present invention for achieving the above object by weight, C: 0.026-0.074%, Si: 0.7-0.9%, Mn: 1.4-1.6%, P: 0.020% or less, S: 0.020% or less, Ti: 1.6-2.1 %, Ni: 0.007% or less, and the balance, the special weld rod molten steel made of Fe and other unavoidable impurity elements, the tundish superheat is maintained to maintain the temperature range of 20-25 ℃, the molten steel The amount of water used during the second cooling of the cast slab, injected into the mold, is in the range of 0.16-0.18 l / kg, and the reduction of the pressed slab in the slab is in the range of 2-2.5 mm, while the total continuous casting speed The technical gist of the continuous casting method for the special welded broom slabs having an excellent internal quality in the range of 0.65-0.75 m / min.
展开▼
机译:本发明涉及一种用于特殊焊丝如CO 2 Sub>焊接,MIG焊接和MAG焊接的大方坯的连续铸造方法。在提供中;为了达到上述重量目的,本发明的C:0.026-0.074%,Si:0.7-0.9%,Mn:1.4-1.6%,P:0.020%以下,S:0.020%以下, Ti:1.6-2.1%,Ni:0.007%以下,其余部分,由Fe和其他不可避免的杂质元素制成的特殊焊条钢水,保持中间包过热度,以保持20-25℃的温度范围,熔融钢水在铸坯的第二次冷却过程中,注入模具的水量在0.16-0.18 l / kg的范围内,铸坯中压制坯的压下量为2-连续铸造总速度为2.5毫米,特殊焊接扫帚板的连续铸造技术要点,其内部质量在0.65-0.75 m / min的范围内。
展开▼