IMPROVED HARDNESS, STRENGTH, AND FRACTURE TOUGHNESS STEEL
IMPROVED HARDNESS, STRENGTH, AND FRACTURE TOUGHNESS STEEL
展开▼
机译:改善的硬度,强度和断裂韧性
展开▼
页面导航
摘要
著录项
相似文献
摘要
A steel article has a composition, by weight percent, including from 0.20 to 0.45 carbon, from 0.4 to 1.5 manganese, from 0.5 to 2.0 silicon, from 0.01 to 2.0 chromium, from 0.15 to 1.2 molybdenum, from 0.01 to 0.40 vanadium, from 0.01 to 0.25 titanium, from 0.005 to 0.05 aluminum, from 0.0001 to 0.010 boron, less than 0.002 oxygen, from 0.005 to about 0.017 nitrogen, and the balance essentially iron. The steel article is free of any detrimental aliminum nitride and has, after quenching and tempering, a fully martensitic microstructure and a controlled distribution of spaced apart micrometer size titanium nitride cuboids and nanometer size background carbonitride precipitates.