Additives of zinc-nickel alloy electroplating bath with good surface quality and plating adhesion and manufacturing method of zinc-nickel electroplated steel sheet using the same
Additives of zinc-nickel alloy electroplating bath with good surface quality and plating adhesion and manufacturing method of zinc-nickel electroplated steel sheet using the same
展开▼
机译:具有良好表面质量和镀层附着力的锌镍合金电镀液添加剂及使用该添加剂的锌镍电镀钢板的制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to an additive of a zinc-nickel alloy electroplating bath and a method of manufacturing a zinc-nickel alloy electroplating steel sheet using the same; The purpose of the present invention is to add a zinc-nickel alloy electroplating bath which exhibits excellent surface quality and plating adhesion when plated on a steel plate, and a method of manufacturing a zinc-nickel alloy electroplating steel sheet using the zinc-nickel alloy electroplating bath containing the additive. In providing.;In order to achieve the above object, the present invention, sodium benzoate or potassium salt: 2-5% by weight, surfactant having a sulfonic group in naphthalene as a Group 1 element salt of the condensation reaction with formaldehyde: 10-25% by weight, the rest Zinc-nickel alloy electroplating with good surface quality and plating adhesion, containing water and sodium benzoate or potassium salt: surfactant in a weight ratio of 1: 1.5 to 3 with P1-toluene sulfonic acid 0.001-0.1 mol / l 0.1-4.0 ml / l of the additive was added to a chloride-based zinc-nickel alloy plating bath having an additive of 20-150 g / l of zinc ion, 0.1-15 g / l of nickel ion temperature, and 100-300 g / l of chlorine ion concentration. Adding; Electroplating the plating solution on a steel plate at a plating bath temperature of 50-70 ° C., pH 1.0-4.5, a current density of 20-180 A / dm 2, and a relative flow rate of 0.5-2.5 m / sec. The present invention relates to a method for manufacturing a zinc-nickel alloy electroplated steel sheet including the same.
展开▼
机译:锌镍合金电镀液的添加剂及使用该添加剂的锌镍合金电镀钢板的制造方法技术领域本发明涉及锌镍合金电镀液的添加剂及其制造方法。本发明的目的是添加一种锌-镍合金电镀浴,其在镀覆到钢板上时具有优异的表面质量和镀敷附着力,以及使用该锌-镍合金制造锌-镍合金电镀钢板的方法。含有添加剂的电镀液。为了实现上述目的,本发明苯甲酸钠或钾盐:按重量计2-5%,在萘中具有磺酸基的表面活性剂作为与甲醛缩合反应的第1族元素盐:10重量百分比为-25%,其余的锌镍合金电镀件具有良好的表面质量和镀层附着力,包含水和苯甲酸钠或钾盐:表面活性剂,重量比为1:1.5至3,并带有P1-甲苯磺酸0.001-0.1 mol / l将0.1-4.0 ml / l的添加剂添加到氯化物基锌镍合金镀液中,该镀液的添加剂为20-150 g / l的锌离子,0.1-15 g / l的镍离子温度,和100-300 g / l的氯离子浓度。添加;在50-70°C的电镀液温度,pH 1.0-4.5、20-180 A / dm 2, Sup>的电流密度和相对流速下在钢板上电镀电镀液0.5-2.5 m /秒锌镍合金电镀钢板的制造方法技术领域本发明涉及一种锌锌合金电镀钢板的制造方法。
展开▼