AlZn melting plated steel sheet null for low temperature burning formation enamel
AlZn melting plated steel sheet null for low temperature burning formation enamel
展开▼
机译:AlZn熔融镀覆钢板,用于低温烧成釉
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To find conditions for preventing the occurrence of blister defect in a porcelain enamel layer at the time of porcelain enameling treatment. ;SOLUTION: The chemical composition of a plating film is limited to that consisting of, by weight, 20-80% Al, 0.1-5% Si, and the balance Zn with inevitable impurities. Moreover, the coating weight of the plating film per side is regulated to (30 to 120) g/m2, and further, the surface roughness of the plating film is controlled so that the center line average height Ra specified by JIS B0601 becomes 0.2 to 2 μm. By this method, the hot-dip Al-Zn coated steel sheet for low temperature firing type porcelain enameling, capable of forming porcelain enamel free from deterioration in antibacterial characteristic and antifugal characteristic with the lapse of time and usable in a wide range of fields, such as plates for building material, kitchen utensils, medical appliances, and chemical vessels, can be obtained.;COPYRIGHT: (C)1999,JPO
展开▼
机译:要解决的问题:寻找在瓷釉处理时防止瓷釉层出现水泡缺陷的条件。 ;解决方案:镀膜的化学成分仅限于以重量计包括20-80%的Al,0.1-5%的Si和余量的Zn和不可避免的杂质。另外,将镀覆膜的每面的涂布重量调整为(30〜120)g / m 2 Sup>,进而,控制镀膜的表面粗糙度,以使中心线平均高度为中心。 JIS B0601规定的Ra为0.2〜2μm。通过这种方法,用于低温烧制型瓷釉的热浸Al-Zn涂层钢板能够形成不会随着时间的流逝而使抗菌特性和抗真菌特性变差的瓷釉,并且可以在广泛的领域中使用,如用于建筑材料,厨房用具,医疗设备和化学容器的板材。;版权所有:(C)1999,JPO
展开▼