Polyethylene resin composition for rotational molding and rotational molded product using the composition
Polyethylene resin composition for rotational molding and rotational molded product using the composition
展开▼
机译:用于滚塑的聚乙烯树脂组合物和使用该组合物的滚塑产品
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a rotational molding polyethylene resin composition which excels in rotational moldability and can prepare rotational molding products having impact resistance and environmental stress cracking resistance superior to those of the conventional polyethylene rotational molding products, and the rotational molding product using the composition. SOLUTION: This rotation molding polyethylene resin composition comprises (A) an ethylene/α-olefin copolymer which has a density of 0.880-0.930 g/cm3 and an MFR of 0.01-5 g/10 min and (B) an ethylene homopolymer or an ethylene/α-olefin copolymer which has a density of 0.931-0.974 g/cm3 and an MFR of 0.5-20 g/10 min, and the weight ratio [(A)/(B)] of the both components is 10/90 to 50/50 and, simultaneously, the density of a blend composed of the both components is 0.920-0.960 g/cm3, and the MFR of the blend is 1-10 g/10 min. It is preferred that component (A) is a copolymer prepared by using a metallocene type olefin polymerization catalyst and component (B) is a (co)polymer prepared by using a metallocene type or Ziegler type olefin polymerization catalyst. Rotational molding products are composed of the polyethylene composition.
展开▼
机译:解决的问题:提供一种滚塑聚乙烯树脂组合物,其具有优异的滚塑性并且可以制备具有比常规聚乙烯滚塑产品的抗冲击性和耐环境应力龟裂性更优异的滚塑产品,以及使用该滚塑聚乙烯产品的滚塑产品。组成。溶液:该旋转模塑聚乙烯树脂组合物包含(A)密度为0.880-0.930 g / cm3和MFR为0.01-5 g / 10 min的乙烯/α-烯烃共聚物,和(B)乙烯均聚物或乙烯/α-烯烃共聚物,其密度为0.931-0.974 g / cm3,MFR为0.5-20 g / 10 min,两种组分的重量比[(A)/(B)]为10 / 90至50/50,同时由两种成分组成的混合物的密度为0.920-0.960 g / cm3,混合物的MFR为1-10 g / 10 min。优选的是,组分(A)是通过使用茂金属型烯烃聚合催化剂制备的共聚物,而组分(B)是通过使用茂金属型或齐格勒型烯烃聚合催化剂制备的(共)聚合物。滚塑产品由聚乙烯组合物组成。
展开▼