Manufacturing method for a colored zirconia based article in particular an orange/red article and a colored zirconia based decorative article obtained in accordance with such method
Manufacturing method for a colored zirconia based article in particular an orange/red article and a colored zirconia based decorative article obtained in accordance with such method
展开▼
机译:着色氧化锆基制品的制造方法,特别是橙/红色制品和根据该方法获得的着色氧化锆基装饰制品
展开▼
页面导航
摘要
著录项
相似文献
摘要
The invention concerns a manufacturing method for an orange/red zirconia article characterised in that it includes the following steps:;forming a mixture including a zirconia powder, 3 to 20% in weight of a stabilising agent, 0.1% to 5% in weight of powders for forming a vitreous phase, including SiO2, Al2O3 and Y2O3, 0.01% to 10% in weight of a copper oxide powder (CuO);;forming a second mixture including said first mixture and a binding agent;;forming a green body of the article from said second mixture;;sintering for at least thirty minutes at a temperature comprised between 1,350 and 1,500° C. in ambiant atmosphere, and;annealing the desired article at a temperature comprised between 700° C. and 1,350° C. for a period of time comprised between 30 minutes and 20 hours in an inert or reducing atmosphere having an oxygen partial pressure comprised between 10−10 and 1 atmosphere, and;polishing said sintered article.
展开▼
机译:本发明涉及一种橙/红氧化锆制品的制造方法,其特征在于它包括以下步骤:形成包含氧化锆粉末,3-20重量%的稳定剂,0.1-5重量%的氧化锆粉末的混合物。用于形成玻璃相的粉末,包括SiO 2 Sub>,Al 2 Sub> O 3 Sub>和Y 2 Sub> O 3 sub>,按重量计0.01%至10%的氧化铜粉末(CuO);;形成包括所述第一混合物和粘合剂的第二混合物;;由所述第二混合物形成制品的生坯;以及在1350到1500℃之间的温度下烧结至少三十分钟。 C.在环境气氛中进行;和;将所需制品在700℃之间的温度下退火。 ℃和1350℃;在氧分压为10 -10 -1的惰性或还原性气氛中,在30分钟至20小时的时间范围内进行抛光;对所述烧结制品进行抛光。
展开▼