Lead silicate glass and a process for setting a reduced surface resistance of the lead silicate glass
Lead silicate glass and a process for setting a reduced surface resistance of the lead silicate glass
展开▼
机译:硅酸铅玻璃和降低硅酸铅玻璃表面电阻的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The invention relates to a lead silicate glass, to the use thereof for the production of secondary electron multipliers, and to a process for setting a reduced surface resistance of a lead silicate glass of this type. The lead silicate glass has the following composition (in % by weight): SiO2 15-35, PbO 35-55, Bi2O320-29, BaO 0-10, Cs2O 0-10, BaO+Cs2O 2-13, CaO 0-10, SrO 0-10, CaO+SrO+BaO 0-10, and up to 1% by weight of conventional fining agents. The surface resistance of the lead silicate glass after reduction in a hydrogen atmosphere is from 0.1 to 60 M&OHgr;/sq.
展开▼
机译:硅酸铅玻璃及其制造方法本发明涉及一种硅酸铅玻璃,其在生产二次电子倍增器中的用途,以及使这种硅酸铅玻璃的表面电阻降低的方法。硅酸铅玻璃具有以下组成(以重量%计):SiO 2 Sub> 15-35,PbO 35-55,Bi 2 Sub> O 3 Sub 20-29,BaO 0-10,Cs 2 Sub> O 0-10,BaO+ Cs 2 Sub> O 2-13,CaO 0-10,SrO 0-10 ,CaO + SrO + BaO 0-10,最高达1%(重量)的常规澄清剂。在氢气氛中还原后,硅酸铅玻璃的表面电阻为0.1至60M&OHgr / sq。
展开▼