PURPOSE: A solution for forming molybdenum/phosphorus/silicate film having excellent corrosion resistance and wettability, and a method for forming molybdenum/phosphorus/silicate film using the same are provided. CONSTITUTION: The method for forming molybdenum/phosphorus/silicate film includes step of heating a solution comprising molybdenum concentration 0.4 to 4.0 g/L, phosphorus concentration 7.0 to 14 g/L, colloidal silica concentration 1.0 to 150 g/L in the temperature range of 40 to 60°C; and immersing galvanized steel sheet in the solution.
展开▼
机译:用途:提供了一种具有优异的耐腐蚀性和润湿性的钼/磷/硅酸盐膜的形成溶液,以及使用该溶液形成钼/磷/硅酸盐膜的方法。组成:钼/磷/硅酸盐膜的形成方法包括以下步骤:在温度范围内加热浓度为0.4至4.0 g / L,磷浓度为7.0至14 g / L,胶体二氧化硅浓度为1.0至150 g / L的溶液40至60℃;并将镀锌钢板浸入溶液中。
展开▼