Method for coating of transport rail of billet with ceramic lubricant in induction furnace
Method for coating of transport rail of billet with ceramic lubricant in induction furnace
展开▼
机译:在感应炉中用陶瓷润滑剂涂覆坯料的运输轨的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention is stainless steel or ceramic lubricants which when moving the steel tube billet for the special steel successively to heat treatment in a high frequency induction furnace to minimize friction between the contact surfaces that are billet sliding possible to prevent surface defects of the billet relates to a rail transfer coating method of the billet for steel pipes using,; That is, according to the billet along the steel rail to the refractory of a high-frequency induction in the heat treatment process for producing a steel pipe of thereby continuously transferred to, SiO₂ powder with a coating for imparting lubricity to the contact surface of the steel rail and the billet 40 Al 2 O₃ component of about -80% 5-20%, B 2 O 3 component 1-20%, CaO 3-25% of component mixing, and the oxygen pressure 20-30psi the mixed powder and acetylene 5-20psi of the rail under the spraying conditions, but heating to 1,000-1,200 ℃ coated with the coating thickness is about 2-3mm, and, heating to 20-30 hours and melted at about 1,200 ℃ the temperature of the coating material on the run.
展开▼
机译:本发明是不锈钢或陶瓷润滑剂,当将用于特殊钢的钢管坯料连续地移至高频感应炉中进行热处理以使坯料滑动的接触面之间的摩擦最小化时,可防止坯料的表面缺陷。钢管坯的钢轨转移涂覆方法,就是说,在热处理过程中,沿着钢轨的钢坯到达高频感应的耐火材料,该热处理过程用于制造钢管,从而连续地转移到具有涂层的SiO 2粉末上,该涂层具有用于赋予润滑脂接触表面的润滑性。钢轨和钢坯的40 Al 2 Sub>O₃成分约占 -80%5-20%,B 2 O Sub> 3成分约1-20%,CaO 3-25%混合,在喷涂条件下,将钢粉和乙炔的混合粉末和乙炔的氧气压力为20-30psi,喷涂条件为5-20psi,但加热至1,000-1,200℃,涂层厚度约为2-3mm,并加热至20- 30小时并在约1200℃的温度下熔化涂料上的涂料。
展开▼