METHOD OF MANUFACTURING Mn/Al VAPOR DEPOSITED GALVANNEALED STEEL SHEET WITH HIGH CORROSION RESISTANCE AND GOOD ELECTROSTATIC PAINTABILITY
METHOD OF MANUFACTURING Mn/Al VAPOR DEPOSITED GALVANNEALED STEEL SHEET WITH HIGH CORROSION RESISTANCE AND GOOD ELECTROSTATIC PAINTABILITY
展开▼
机译:具有高耐蚀性和良好静电性的Mn / Al气相沉积镀锌钢板的制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: A method of manufacturing Mn/Al vapor deposited galvannealed steel sheet with high corrosion resistance and good electrostatic paintability is provided. CONSTITUTION: In a method of manufacturing Mn/Al vapor deposited galvannealed steel sheet with high corrosion resistance and good electrostatic paintability, the method is characterized in that a galvannealed steel sheet is heated to 100-350 deg.C; aluminum is vacuum-deposited on each side of galvannealed steel sheet in an amount of less than 10 g/m¬2; and manganese is vacuum-deposited thereon in an amount of 3 to 10 g/m¬2.
展开▼
机译:目的:提供一种制造具有高耐腐蚀性和良好的静电可涂性的Mn / Al气相沉积镀锌钢板的方法。组成:一种具有高耐蚀性和良好的静电可涂性的Mn / Al气相沉积镀锌钢板的制造方法,其特征在于,将镀锌钢板加热至100-350℃。铝以小于10 g / m 2的量真空沉积在热镀锌钢板的每一面上。并且将锰以3至10g / m 2的量真空沉积在其上。
展开▼