NICKEL-CHROMIUM-MOLYBDENUM ALLOY RESISTANT TO LOCAL CORROSION DUE TO WET-TREATED PHOSPHORIC ACID AND CHLORIDE
NICKEL-CHROMIUM-MOLYBDENUM ALLOY RESISTANT TO LOCAL CORROSION DUE TO WET-TREATED PHOSPHORIC ACID AND CHLORIDE
展开▼
机译:镍铬钼合金由于经过湿法处理的磷酸和氯化物而对局部腐蚀有抵抗力
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a novel alloy which has a higher composite resistance to local corrosion due to wet-treated phosphoric acid and chlorides than a conventional alloy and does not need the addition of tungsten, tantalum, or copper reducing the thermal stability.;SOLUTION: This nickel-chromium-molybdenum alloy contains 31.0-34.5 wt.% chromium, 7.0-10.0 wt.% molybdenum, 0.2 wt.% or lower nitrogen, 3.0 wt.% or lower iron, 1.0 wt.% or lower manganese, 0.4 wt.% or lower aluminum, 0.75 wt.% or lower silicon, 0.1 wt.% or lower carbon, and the balance being nickel and impurities.;COPYRIGHT: (C)2004,JPO