The change process of physically - quu00ecmicas properties of a plant extract of Acacia, Mimosa, plant extract, modified, and the use of a chemically modified plant extract
The change process of physically - quu00ecmicas properties of a plant extract of Acacia, Mimosa, plant extract, modified, and the use of a chemically modified plant extract
"The change process of physically - quu00ecmicas properties of a plant extract of Acacia, Mimosa, plant extract, modified, and the use of a chemically modified plant extract.The present invention relates to a process of modification of physical and chemical properties of a plant extract of Acacia, MimosaFor tanning and retanning of leather which comprises: (a) mixing an extract in powder extracted from the black Acacia with water at a ratio of about 0.5 to 2.0 kg / 1 of water,Preferably in the ratio of 1.0 to 1.5 kg / L, and more preferably 1.05 to 1.06 kg / L; or alternatively, using a solution of tannin in liquid form at a concentration of 25% to 60%.Preferably in a concentration of 45% to 55%.And more preferably in a concentration of 50% in total solids; (b) heating the mixture formed under intense agitation to a temperature between 50 and 100 198 C,And preferably between 67 and 98 198 C; (c) adding slowly a sulfonation agent to the heated mixture in a ratio by weight of about 1 / 100 to about 1 / 20 to the Black Wattle Extract; and(d) to elevate the temperature of the mixture to a range between 45 and 135 198 C, maintaining a pressure between 0.2 kgf / cm ^ 2 ^ and 7 kgf / cm ^ 2 ^ for a period between 1 and 14 hours to complete the sulfonation of tannin.
展开▼
机译:相思树,含羞草,植物提取物的植物提取物的物理-化学特性的变化过程,以及化学修饰的植物提取物的用途。本发明涉及物理和化学性质的修饰方法用于鞣制和复鞣皮革的含羞草相思植物提取物,其包括:(a)将提取自黑相思树的粉末中的提取物与水以约0.5至2.0 kg / 1的水比例混合,优选比例为浓度为1.0至1.5 kg / L,更优选1.05至1.06 kg / L;或者使用浓度为25%至60%的液体单宁溶液,优选浓度为45%至55 (b)将剧烈搅拌下形成的混合物加热到50至100 <198> C,优选67至98 <198> C;(c) )以重量比o向加热的混合物中缓慢添加磺化剂f黑荆芥提取物的含量约为1 / 100至约1 / 20; (d)将混合物的温度升高至45至135 <198> C,并保持0.2 kgf / cm ^ 2 ^至7 kgf / cm ^ 2 ^的压力持续1至2分钟。 14小时完成单宁的磺化。
展开▼