POLYHEDRAL MULTI-LAYER CARBON FULLEROID NANOSTRUCTURES

摘要

The inventive polyhedral multi-layer carbon fulleroid nanostructures have distinctive interlayer distance of 0.34-0.36 nm, a mean particle size ranging from 60- to 200 nm, a bulk density of 0.6-0.8 g/cm3, a pycnometric density of 2.2±0.1 g/cm3, an index of thermobarostability with respect to graphitization equal to or higher than 50 Kbar at a temperature of 3000 °C, a roengenographic graphitization index of 0.001-0.002, a specific electric resistance equal to or less than 2.5x10-4 Om.m at a pressure of 120 MPa.