METHOD FOR MANUFACTURING HYDROPHILIC COATED GLASS, WHICH CAN MAINTAIN HYDROPHILICITY DUE TO PHOTOCATALYTIC FUNCTION OF TITANIUM DIOXIDE AND HYGROSCOPIC PROPERTY OF SILICA
METHOD FOR MANUFACTURING HYDROPHILIC COATED GLASS, WHICH CAN MAINTAIN HYDROPHILICITY DUE TO PHOTOCATALYTIC FUNCTION OF TITANIUM DIOXIDE AND HYGROSCOPIC PROPERTY OF SILICA
展开▼
机译:制备亲水涂层玻璃的方法,由于二氧化钛的光催化作用和二氧化硅的吸湿性能,该玻璃可以保持亲水性
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE: A method for manufacturing hydrophilic coated glass is provided to show and maintain hydrophilicity resulting from a photocatalytic function of titanium dioxide and hygroscopic property of silica, and to improve the restorability of hydrophilicity. CONSTITUTION: The method for manufacturing hydrophilic coated glass comprises coating the glass surface with titanium dioxide and silica. Particularly, the method comprises the steps of: coating glass with a titanium dioxide solution and heat treating it at 400-600 deg.C for 1-2 hours; and coating the surface of glass coated with titanium dioxide with a silica solution and heat treating it at 200-600 deg.C for 20 min-1 hour. The hydrophilic coated glass has a double hydrophilic coating layer formed of a titanium dioxide layer having a thickness of 0.1-0.5 micrometers and a silica layer with a thickness of several angstroms.
展开▼