EDGE-ON STRESS-RELIEF OF THICK ALUMINIUM PLATES.

摘要

In accordance with the present invention, there are provided methods for the manufacture of aluminum alloy plates having reduced levels of residual stress, comprising: providing a solution heat-treated and quenched aluminum alloy plate with a thickness of at least 5 inches, and stress relieving the plate by performing at least one compressing step at a total rate of 0.5 to 5 % permanent set along the longest or second longest edge of the plate. In the method, the dimension of the plate where the compression step is performed is along the longest or second longest edge of the plate, which is preferably no less than twice and no more than eight times the thickness of the plate. In further accordance with the present invention, there are provided stress-relieved alloys and plates that are provided with superior Wtot properties as well as reduced residual stress and heterogeneity values.