RESIN COMPOSITION FOR FORMING FOAMED POLYOLEFIN RESIN SHEET AND FOAMED POLYOLEFIN RESIN SHEET PRODUCED THEREFROM
RESIN COMPOSITION FOR FORMING FOAMED POLYOLEFIN RESIN SHEET AND FOAMED POLYOLEFIN RESIN SHEET PRODUCED THEREFROM
展开▼
机译:用于形成泡沫聚烯烃树脂板的树脂组合物和由其制备的泡沫聚烯烃树脂板
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a foamed polyolefin resin sheet having thin thickness, high expansion ratio, fine cell size and good surface smoothness.;SOLUTION: The resin composition for forming a foamed polyolefin resin sheet contains (A) 40-70 wt% polypropylene resin, (B) 10-30 wt% polybutene-1 resin, (C) 5-20 wt% ethylene-α-olefin copolymer having a density of 0.87-0.89 g/cm3 and (D) 5-25 wt% inorganic filler.;COPYRIGHT: (C)2006,JPO&NCIPI
展开▼
机译:要解决的问题:提供一种具有薄的厚度,高的膨胀率,细的泡孔尺寸和良好的表面光滑度的泡沫聚烯烃树脂片材;解决方案:用于形成泡沫聚烯烃树脂片材的树脂组合物包含(A)40-70重量%聚丙烯树脂;(B)10-30 wt%的聚丁烯-1树脂;(C)5-20 wt%的乙烯-α-烯烃共聚物,密度为0.87-0.89 g / cm 3 Sup>; (D)5-25 wt%的无机填料。;版权所有:(C)2006,JPO&NCIPI