Composition of film envelope for growing clean agricultural products, method for fabricating the same, and cultivation method for clean agricultural products

摘要

Disclosed are a synthetic resin film envelope and a cultivating method for clean agricultural products. The synthetic resin film envelope is formed with a double-layer sectional structure having a thickness of about 0.02 to 0.1 mm and includes 60 to 90 weight percent of polypropylene resin having a melt index of 3 to 10 g/min at a temperature of 185° C., 1 to 20 weight percent of an antifogging agent, 1 to 10 weight percent of an antistatic agent, and 1 to 10 weight percent of white carbon.