UV-absorbing borosilicate glass for a gas discharge lamp, process for manufacturing same and gas discharge lamp made with same
UV-absorbing borosilicate glass for a gas discharge lamp, process for manufacturing same and gas discharge lamp made with same
展开▼
机译:用于气体放电灯的吸收紫外线的硼硅酸盐玻璃,其制造方法以及由该玻璃制成的气体放电灯
展开▼
页面导航
摘要
著录项
相似文献
摘要
Glass for gas discharge tubes, which are used in fluorescent lamps, EEFL lamps, LCD displays, computer monitors, telephone displays and TFT displays, and a process for making it are described. The glass contains, in % by weight based on oxide content: SiO2, 60-75; B2O3, 25-35; Al2O3, 0-10; Li2O, 0-10; Na2O, 0-20; K2O, 0-20; MgO, 0-8; CaO, 0-20; SrO, 0-5; BaO, 0-5; ZnO, 0-3; ZrO2, 0-5; TiO2, 0-10; Fe2O3, 0-0.5; CeO2 0-0.5; MnO2, 0-1.0; Nd2O3, 0-1; WO3, 0-2; Bi2O3, 0-5; MoO3, 0-5; As2O3, 0-1; Sb2O3, 0-1; SO42−, 0-2 C−, 0-2 and F−, 0-2, wherein ΣLi2O+Na2O+K2O=0-25% by weight; ΣMgO+CaO+SrO+BaO=0-20; ΣFe2O3+CeO2+TiO2+PbO+As2O3+Sb2O3 is at least 0-10; and ΣPdO+PtO3+PtO2+PtO+RhO2+Rh2O3+IrO2+Ir2O3 is from 0.00001-0.1.
展开▼
机译:描述了用于荧光灯,EEFL灯,LCD显示器,计算机显示器,电话显示器和TFT显示器中的气体放电管的玻璃及其制造方法。该玻璃包含基于氧化物含量的以重量%计的SiO 2 Sub>,60-75;和B 2 Sub> O 3 Sub>,> 25-35; Al 2 Sub> O 3 Sub>,0-10; Li 2 Sub> O,0-10; Na 2 Sub> O,0-20; K 2 Sub> O,0-20;氧化镁,0-8;氧化钙,0-20; SrO,0-5; BaO,0-5; ZnO,0-3; ZrO 2 Sub>,0-5; TiO 2 Sub>,0-10; Fe 2 Sub> O 3 Sub>,0-0.5; CeO 2 Sub> 0-0.5; MnO 2 Sub>,0-1.0; Nd 2 Sub> O 3 Sub>,0-1; WO 3 Sub>,0-2; Bi 2 Sub> O 3 Sub>,0-5; MoO 3 Sub>,0-5; As 2 Sub> O 3 Sub>,0-1; Sb 2 Sub> O 3 Sub>,0-1; SO 4 Sub> 2-−Sup>,0-2 C - Sup>,0-2和F - Sup>,0-2,其中ΣLi 2 Sub> O + Na 2 Sub> O + K 2 Sub> O = 0-25%(重量); ΣMgO+ CaO + SrO + BaO = 0-20; ΣFe 2 Sub> O 3 Sub> + CeO 2 Sub> + TiO 2 Sub> + PbO + As 2 Sub> O 3 Sub> + Sb 2 Sub> O 3 Sub>至少为0-10;和ΣPdO+ PtO 3 Sub> + PtO 2 Sub> + PtO + RhO 2 Sub> + Rh 2 Sub> O 3 < / Sub> + IrO 2 Sub> + Ir 2 Sub> O 3 Sub>是0.00001-0.1。
展开▼