Thermally conductive polymer compositions having moderate tensile and flexural properties
Thermally conductive polymer compositions having moderate tensile and flexural properties
展开▼
机译:具有适度的拉伸和挠曲性能的导热聚合物组合物
展开▼
页面导航
摘要
著录项
相似文献
摘要
A thermally conductive polymer composition having enhanced mechanical properties is provided. The polymer composition consists of a base polymer matrix loaded with fillers that results in a thermal conductivity that is greater than 1.5 W/m°K and a tensile modulus within an acceptable range making the composition suitable for structural plastic applications, such as between 1,700 to 12,000 Mpa and more preferably between approximately 2,700 to 10,000 Mpa and even more preferably in the range of between approximately 4,000 to 9,000 Mpa. In addition to a tensile modulus within the identified range the composition also includes an elongation to break value that is at least above 1.0% and more preferably in the range of about 1.2% to 10%.
展开▼
机译:提供了具有增强的机械性能的导热聚合物组合物。聚合物组合物由填充有填料的基础聚合物基质组成,该填料导致的导热系数大于1.5 W / m°K,拉伸模量在可接受的范围内,从而使该组合物适用于结构塑料应用,例如1,700至12,000 Mpa,更优选在大约2,700至10,000 Mpa之间,甚至更优选在大约4,000至9,000 Mpa的范围内。除了在所确定的范围内的拉伸模量之外,该组合物还包括至少大于1.0%并且更优选在约1.2%至10%的范围内的断裂伸长率值。
展开▼