Granulated Blast Furnace Slag, Fine Aggregate Obtained Therefrom, And Manufacturing Method Thereof
Granulated Blast Furnace Slag, Fine Aggregate Obtained Therefrom, And Manufacturing Method Thereof
展开▼
机译:粒状高炉矿渣,由此获得的细骨料及其制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Novel granulated blast furnace slag, which has a mass per unit volume of at least 1.45 kg/l and a fineness modulus of at least 3.7, can be simply and effectively obtained by causing blast furnace slag of 1350 to 1400 DEG C to flow at a quantity of flow of 2 to 5 ton/min and by ejecting water to the slag at a flow velocity of 5 to 8 m/sec and at a rate of quantity of flows by weight of water/slag of 7 to 15. Since the granulated blast furnace slag has a high grain size and a high density which cannot be obtained conventionally, it can be preferably used as fine aggregate for concrete when the grain size thereof is adjusted by crushing/grinding, or the like. IMAGE
展开▼
机译:通过使1350-1400℃的高炉矿渣流过,可以简单有效地得到新型粒状高炉矿渣,其单位体积质量至少为1.45kg / l,细度模量至少为3.7。流量为2至5吨/分钟,并以5至8 m / sec的流速将水喷射到炉渣中,并且流量以水/炉渣的重量计的流量为7至15。高炉矿渣具有以往无法获得的高粒径和高密度,当通过粉碎/研磨等来调节其粒径时,可以优选用作混凝土的细骨料。 <图像>
展开▼