Method for producing SiC fiber-reinforced SiC composite material by means of hot press
Method for producing SiC fiber-reinforced SiC composite material by means of hot press
展开▼
机译:热压生产SiC纤维增强SiC复合材料的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
A powdery mixture of fine SiC powder with one or more oxide sintering additives of Al2O3, Y2O3, SiO2 and CaO is blended and uniformly dispersed in a polymeric SiC precursor to prepare a matrix-forming polymeric slurry. A preform of SiC fiber, which has quasi-stoichiometric composition with high crystallinity, is impregnated with the polymeric slurry and then hot-pressed at a temperature of 1600° C. or higher in presence of a liquid phase. Since the heat-resistant SiC fiber is used as strengthening fiber, the prepreg is sintered to a dense SiC composite excellent in mechanical properties by one-step hot-pressing.
展开▼
机译:SiC细粉与Al 2 Sub> O 3 Sub>,Y 2 Sub> O 3 的一种或多种氧化物烧结添加剂的粉末混合物将Sub>,SiO 2 Sub>和CaO混合并均匀分散在聚合物SiC前驱体中,以制备形成基质的聚合物浆料。将具有高结晶度的准化学计量组成的SiC纤维的预成型件用聚合物浆料浸渍,然后在液相存在下在1600℃或更高的温度下热压。由于将耐热性SiC纤维用作强化纤维,因此,预浸料通过一步热压而被烧结为机械特性优异的致密的SiC复合材料。
展开▼