Brazing articles of stainless steel, e.g. large heat exchanger involves applying an iron-based brazing filler material to parts of stainless steel, heating the parts, and providing brazed areas with specific average hardness
Brazing articles of stainless steel, e.g. large heat exchanger involves applying an iron-based brazing filler material to parts of stainless steel, heating the parts, and providing brazed areas with specific average hardness
Brazing articles of stainless steel involves applying an iron-based brazing filler material to parts of stainless steel; optionally assembling the parts; heating the parts to at least 1000[deg]C in a non-oxidizing atmosphere, a reducing atmosphere and/or vacuum, and heating the parts to at least 1000[deg]C for at least 15 minutes; providing articles having an average hardness of less than 600 HV1 of the obtained brazed areas; and optionally repeating one or more of applying step, assembling step and heating step. An independent claim is also included for a brazed article of stainless steel comprising at least one base material of stainless steel and an iron-based brazing filler material. The obtained brazed areas, pores, cracks, gaps, joints, or crevices have a tensile strength of at least 110 N/mm 2 and an average hardness of less than 600 HV1.
展开▼
机译:不锈钢的钎焊制品包括将铁基钎料填充到不锈钢零件上。可选地组装零件;在非氧化性气氛,还原性气氛和/或真空中将部件加热至至少1000℃,并且将部件加热至至少1000℃至少15分钟;提供所获得的钎焊区域的平均硬度小于600 HV1的物品;以及任选地重复施加步骤,组装步骤和加热步骤中的一个或多个。对于包括至少一种不锈钢基体材料和铁基钎焊填充材料的不锈钢钎焊制品,也包括独立权利要求。所获得的钎焊区域,孔,裂纹,间隙,接缝或缝隙具有至少110N / mm 2的拉伸强度和小于600HV1的平均硬度。
展开▼