Hot stamping procedure parts Al-Mg alloy.
Hot stamping procedure parts Al-Mg alloy.
展开▼
机译:热冲压程序零件为Al-Mg合金。
展开▼
页面导航
摘要
著录项
相似文献
摘要
Process for manufacturing drawn parts made of aluminum alloy comprising the following steps: - manufacturing a strip of thickness between 0.5 and 5 mm alloy composition (weight%): Mg: 6.1 Mn 1 2 Cu 1 Zn 1 If 3 Fe 2 Cr 0.4 Zr 0.3 with a content of other elements 0.1 each and 0.5 total, the remainder being Al, - cutting a blank from this strip, - local or total heating of the blank to a temperature between 150 and 350 ° C and a duration 30 s, - stuffing the blank heated by a jig heated to least partially, at a temperature between 150 and 350 ° C, in the presence of a lubricant compatible with subsequent operations.
展开▼
机译:用于制造由铝合金制成的拉制零件的方法,包括以下步骤:-制造厚度在0.5至5毫米之间的合金成分(重量%)的带:Mg:6.1 Mn <1 2 Cu <1 Zn <1 If <3 Fe < 2 Cr <0.4 Zr <0.3,其他元素含量分别<0.1和<0.5,其余为Al,-从该带材上切下一个坯料,-将坯料局部或全部加热至150至350°C持续时间小于30 s,-在150-350℃之间的温度下,在与后续操作兼容的润滑剂存在下,填充由至少部分加热的夹具加热的坯料。