METHOD OF MANUFACTURING APPROXIMATELY NANO-DEGREE OXIDE OBTAINED BY THERMAL DECOMPOSITION METHOD FOR METAL
METHOD OF MANUFACTURING APPROXIMATELY NANO-DEGREE OXIDE OBTAINED BY THERMAL DECOMPOSITION METHOD FOR METAL
展开▼
机译:制造金属热分解法获得的近似纳米氧化物的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a method of manufacturing an approximately nano-degree thermal decomposition method oxide having a minimal chloride content and a BET surface area of 1-600 m2/g without necessitating an extremely high vaporization temperature.;SOLUTION: This oxide is obtained by dissolving an organic metal material in a solvent and converting it into an oxide in a flame at a temperature over 200°C.;COPYRIGHT: (C)2009,JPO&INPIT
展开▼
机译:要解决的问题:提供一种制备具有大约纳米级热分解法的氧化物的方法,该氧化物具有最低的氯化物含量和BET表面积为1-600 m 2 Sup> / g,而无需非常高解决方案:该氧化物是通过将有机金属材料溶解在溶剂中并将其在温度超过200℃的火焰中转化为氧化物而获得的;版权所有:(C)2009,JPO&INPIT